• COROSSION RESISTANT LININGS

Corrosion resistant linings are used to provide protection to process equipment and structures made of carbon steel, concrete or other subtract, from the effects of corrosion. Process equipment made of carbon steel and protected with appropriate rubber lining, is usually more economical than the same equipment fabricated from an alloy or more corrosion resistant metal such as titanium or tantalum. Therefore, rubber lining is accepted worldwide, for anti-corrosive protective coating, due to its proven superiority in service and relatively low cost.

LeBracs Rubber has a variety of Rubber compounds, both of Natural and Synthetic grade made with special chemicals and additives to serve under highly corrosive conditions, undergoing high temperatures and pressures.

LeBracs Rubber provides surface protection for many applications to industries in the core sectors, such as:



ON SITE RUBBER LINING

LeBracs Rubber has executed several onsite linings, usingcold bonding as well as hot bonding methods.



DM WATER STORAGE TANKS

  • Rubber Compound:
    Soft Natural Rubber 65 ± 5° Shore "A"

  • Rubber Sheet thickness:
    3 mm


CAUSTIC STORAGE TANK

  • Rubber Compound:
    Butyl Soft 52 ± 5° Shore "A"

  • Rubber Sheet thickness:
    6 mm


HCL STORAGE TANK

  • Rubber Compound:
    Butyl Soft 60 ± 5° Shore "A"

  • Rubber Sheet thickness:
    5 mm


CLARIFIER

  • Rubber Compound:
    Soft Natural 52 ± 5° Shore "A"

  • Rubber Sheet thickness:
    4.5 mm


CONCRETE PITS

  • Rubber Compound:
    Butyl Soft 60 ± 5° Shore "A"

  • Rubber Sheet thickness:
    5 mm
CODE NO TYPE OF RUBBER SERVICE CONDITION HARDNESS RANGE TEMPERATURE
LRL 5060SM Natural Soft Rubber Phosphoric Acid service 55 ± 5º Shore 'A' 65° C
LRL TRIFLEX Natural Soft Rubber Pipe Lines for Phosphoric Acid, Any Dilute Acid 60 ± 5º Shore 'A' 70° C
LRL 6070S Natural Soft Rubber DM Water service 65 ± 5ºShore 'A' 75° C
LRL BY50 Synthetic Soft Rubber HCLService, Caustic Storage, Soda Ash, Phos. Acid service 52 ± 5ºShore ‘A’ 100° C
LRL CBY50 Synthetic Soft Rubber Ferric Chloride Service 52 ± 5ºShore ‘A’ 115° C
LRL BBY50 Synthetic Soft Rubber Flue Gas Desulphurization 55 ± 5ºShore ‘A’ 100° C
LRL 6070N Synthetic Soft Rubber Hydro Flousilicic Acid & Sea Water 65 ± 5ºShore ‘A’ 90° C
LRL 6070B Natural Hard Rubber Semi Water Treatment & ETP Service 65 ± 5º Shore ‘D’ 70° C
LRL 8090 Natural Hard Rubber (Ebonite) Brine Solution, 33 % HCL, Caustic Lye, Dyes 75 ± 5º Shore ‘D’ 80° C
LRL CMS8090
(Low Ca,Mg,Si)
Natural Hard Rubber (Ebonite) Pure Brine , Polished Brine Storage Tank 70 ± 5º Shore ‘D’ 80° C
LRL 6070 N – Synthetic Soft Rubber Potable Water, Desalination & Food Grade application 65 ± 5ºShore ‘A’ 90° C

NOTE:
Technical Parameters may be changed due to continuous product development. Thickness of Rubber Sheets: Rubber Sheets are normally manufactured in the thickness range of 1mm to 20mm, with a tolerance of ±5% LeBracs Rubber has in addition to the above, special compounds of Rubber Sheets for other service conditions.